Poromechanical analysis of oil well cements in CO2-rich environments

Juan Cruz Barría (1, 2) , Mohammadreza Bagheri (3) , Diego Manzanal (4) , Seyed M Shariatipour (3) , Jean-Michel Pereira (2)

1 UNPSJB - Universidad Nacional de la Patagonia San Juan Bosco
2 NAVIER UMR 8205 - Laboratoire Navier
3 Coventry University
4 ETSI Caminos, Canales y Puertos

Wells drilled in carbon storage sites could be converted to potential leakage pathways in the presence of CO 2bearing fluids and under the impact of the changes occurring in underground stress. To test this hypothesis, in this study, the behavior of Class G oil well cement in contact with supercritical CO 2 has been investigated. The cement cores were cured under lime-saturated water for 28 days at a temperature of 20 ∘ C and under atmospheric pressure. Subsequently, they were exposed to supercritical CO 2 under a pressure of 20 MPa and at a temperature of 90 ∘ C for 30 days. The penetration depth of the carbonation front and the change in the poromechanical properties of the cement core were measured against time. A numerical modeling exercise has also been conducted to simulate the alteration within the cement cores. The results presented in this study show that the precipitation of calcium carbonates reduces the porosity within the outermost layers of the cement cores. This phenomenon shifts the main pore size class towards smaller sizes. In contrast to expectations, the reduction in porosity does not improve the overall strength of the cement specimens. The observed reduction in the strength of the cement specimens might be associated with either the amorphous structure of the precipitated carbonates or the weak bonding between them and the solid walls of the pores and the high degradation of calcium silicate hydrates.

Mots clés: Supercritical carbonation; Class G cement; Poromechanical behavior; Numerical modeling

Domaines: Mécanique des matériaux [physics.class-ph]

Juan Cruz Barría, Mohammadreza Bagheri, Diego Manzanal, Seyed M Shariatipour, Jean-Michel Pereira. Poromechanical analysis of oil well cements in CO2-rich environments. International Journal of Greenhouse Gas Control, 2022, 119, pp.103734. ⟨10.1016/j.ijggc.2022.103734⟩. ⟨hal-03905356⟩