Supercritical drying of cementitious materials

Zhidong Zhang


Techniques to characterize the microstructure of hydrated cement require dried materials. However, the microstructure of hydrated products is significantly altered by high capillary forces during drying when using the conventional drying methods. To avoid drying stresses when preparing samples, we have employed supercritical drying (SCD) which has been used for decades to prepare aerogels that undergo no shrinkage during drying, but has rarely been used for cementitious materials. The pore solution is first replaced with isopropanol, and then with trifluoromethane (R23). The temperature and pressure are raised above the critical point, where no menisci or capillary pressure can exist; therefore, the dried samples are free of artifacts created by stresses. Images from scanning electron microscope show less compact morphology for supercritically dried samples than that dried by conventional methods, while BET surface areas of SCD samples are very close to samples dried by isopropanol replacement method. This can be explained by the fact that isopropanol and supercritical fluid enter the micropores and block them. The nature of the chemical interactions of isopropanol and R23 with cement pastes are still not clear, but no reaction products were identified in the present study.
Fichier principal
Vignette du fichier
CCR2017_SCD_experiment.pdf (15.98 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-01622913 , version 1 (24-10-2017)



Zhidong Zhang, George W Scherer. Supercritical drying of cementitious materials. Cement and Concrete Research, 2017, 99, pp.137-154. ⟨10.1016/j.cemconres.2017.05.005⟩. ⟨hal-01622913⟩


124 Consultations
453 Téléchargements



Gmail Facebook Twitter LinkedIn More